Nickel plating at home (chemical and galvanic)

Nickel plating is the most popular electroplating process. Attractive appearance, high corrosion resistance and mechanical properties speak in favor of the wider use of nickel for decorative, protective and functional purposes.

Nickel applied directly to steel is in the nature of a cathodic coating and therefore protects only mechanically. The discontinuity of the coating contributes to the formation of corrosive couples, in which steel is a soluble electrode. This results in corrosion under the plating, which erodes the steel substrate and causes the nickel plating to peel off. In order to prevent this phenomenon, the steel must be coated with a dense, non-porous, thick layer of nickel.

Nickel coatings are the basis of multilayer decorative and protective systems Ni-Cr and Cu-Ni-Cr. The use of baths with shine formers greatly simplifies the technology of applying multilayer coatings.

Due to its high mechanical properties, nickel is used to restore worn machine parts, galvanoplastic production of injection molds, and structural elements that are difficult or even impossible to produce using conventional mechanical methods. In the chemical industry, a thick layer of nickel is used to cover parts exposed to strong alkalis.

Nickel plating baths

Widely used in workshops is a bath consisting of three main components: nickel sulfate, boric acid and chloride, such as nickel.

Nickel sulfate is a source of nickel ions. Nickel chloride significantly affects the performance of nickel anodes. In chloride-free baths, strong passivation of nickel occurs, as a result of which the nickel content in the bath decreases, and the result is a decrease in current efficiency and deterioration in the quality of coatings. In the presence of chlorides, the anodes dissolve to a degree sufficient for normal nickel plating. Chlorides increase the conductivity of the bath and the “operability” of the bath when contaminated with zinc. Boric acid makes it easier to maintain pH at the same level. The effectiveness of this action largely depends on the concentration of boric acid (in practice, predominantly ~30 g/l).

The use of nickel chloride is not considered desirable by everyone. Due to its high price, and often difficulty of acquisition. However, it is necessary to take into account that when introducing nickel chloride into the bath, we also introduce nickel into the bath. NiCl2•6H2O chloride theoretically contains 24.69% nickel and, therefore, by introducing this chloride in an amount of 40 g/l, we increase the nickel content in the bath by approximately 10 g/l, which already has a certain value.

Another frequently debated issue is the use of sodium chloride as a source of chlorides. It is known that many electroplating shops successfully introduce NaCl into bright nickel plating baths.

There are many reasons for poor performance of nickel baths, and the claim that the reason is the use of table salt has little justification. Even the English company Canning, well known among electroplating technicians, introduces sodium chloride in the amount of 28 g/l into the NiSOL bright nickel plating bath. Instead of sodium chloride, another chloride can be used, for example, as in PNR, magnesium chloride. The Watts sulphate bath has been known and widely used for many years. The contents of individual components - the basis of Watts baths for applying matte coatings are, g/l: (200-350) NiS04•7H20, (30-60) NiС12•6H20, (25-40) H3BO3.

Often, additives of so-called electrically conductive salts are added to the Watts bath, which increase the electrical conductivity of the bath and improve the appearance of the coating. Among these salts, the most commonly used is magnesium sulfate (~30 g/l); in baths for mass treatment of small parts, its concentration is much higher.

Nickel sulfate is most often introduced in a concentration of 250-350 g/l. For a long time, an upper concentration limit was considered appropriate, which made it possible to carry out the process at high current densities without fear of burning the coating on the ribs and protruding areas. Recently, there has been a tendency to limit nickel sulfate to less than 200 g/l, which significantly reduces solution losses.

The concentration of chlorides in a nickel bath is not precisely standardized. In so-called chloride baths the concentration of nickel chloride exceeds 200 g/l and therefore there is no need to add nickel sulfate. In a workshop environment this is not justified, even based on the price of nickel chloride.

The concentration of boric acid reaches 25-40 g/l. Below 25 g/l the tendency for the nickel bath to become alkalized rapidly increases. However, exceeding a level of 40 g/l may be unfavorable due to the possibility of boric acid crystallizing in the form of crystals deposited on the walls of the bath and anodes. This phenomenon occurs especially easily in unfavorable or poorly heated baths.

The sulfate bath operates over a wide range of temperatures, current densities and pH. At room temperature, nickel plating is rarely used. For coatings applied in cold baths, nickel peeling off along with the chromium often occurs during decorative chrome plating. Therefore, the bath should be heated to at least 30 °C.

The bath with blackening agents operates at 50-60 °C. The current density must be selected experimentally so that coatings are not burned.

The sulfate bath works reliably over a wide pH range. Previously, baths were usually maintained at a pH value of 5.4–5.8, which was motivated by the less aggressiveness and better hiding power of the bath. However, such a high pH value leads to a significant increase in stress in nickel coatings. Therefore, in most baths used in industry, pH = 3.5–4.5.

Modern baths require mixing, which is necessary from the point of view of intensifying the nickel plating process and reducing the risk of pitting. Stirring the bath entails the need for continuous filtration in order to eliminate mechanical impurities.

Mixing with a moving cathode rod is not as effective as mixing with compressed air, and in addition, it requires a special ingredient that prevents foaming. Accordingly, purified air is currently used in the galvanic workshops of Poland to mix all nickel baths equipped with devices for bright nickel plating, manufactured at the Institute of Precision Mechanics.

What is nickel plating used for?

The scope of application of nickel plating is very wide and varied. One of the main objectives of the process is to increase the service life of the product, because nickel coating protects the metal from many negative factors. Increases resistance to corrosion, wear, moisture and oxidation. Also, some special operating conditions for parts require the application of nickel.

After nickel plating of the metal, its surface may have a glossy or matte finish. In practice, glossy is more often used, since if copper plating is carried out first, polishing will not be required later. In addition to nickel plating, in some cases it is advisable to galvanize the metal. Galvanizing of metal in Moscow can be done inexpensively in our company 5 Vitkov.

Advantages

The surface shell, which is formed after the nickel plating process, has a number of positive practical qualities:

• resists the process of metal corrosion;
• oxidation by air;
• aggressive environments such as alkaline and acidic;
• increases strength and resistance to wear and high temperatures;
• aesthetically improves the appearance of the part.

Also, one of the main advantages is, of course, the price of nickel plating. Compared, for example, with processes such as chrome plating, the cost of nickel plating will significantly save your budget. Nickel plating is ideal as a preliminary layer before applying other coatings, and thus protects the top layer from peeling. Our company 5 Vitkov produces custom-made electrical discharge cutting of metal. If you are interested in this service, you can learn more about it from our managers.

General characteristics of bright nickel-plated baths.

Traditional baths for applying matte coatings are currently used indefinitely. They are used, in particular, for pre-nickel plating of steel products before acid copper plating, in the belief that on matte nickel the matte coating deposited in an acid bath has better adhesion than on bright nickel. This assumption is sometimes justified, since decomposition products of organic additives accumulate in baths with brightening agents, leading to passivation of nickel coatings, mainly in galvanic workshops, whose workers neglect the rules for preserving nickel baths that have been used for a long time without regeneration.

However, there is a situation that forces one to abandon nickel plating in baths with shine-forming additives, for the reason that shiny coatings are not flexible enough and are destroyed when nickel-plated objects are bent. Before deciding to use bright nickel plating in series production, the suitability of the process must first be tested on samples.

Nickel plating price

The appearance and durability of each part is what every hardware manufacturer cares about. And it doesn’t matter at all whether it’s car parts, plumbing products, screws, bolts, nuts, etc. Quality always comes first. When ordering nickel plating of parts in Moscow, you take care of the quality of your products, your reputation and your budget. You can find out more about our prices by calling our line or filling out the feedback form on our website, and we will call you back!

Consumption of nickel anodes.

Practitioners who deal with nickel plating on a daily basis know that nickel consumption is associated mainly with the consumption of nickel anodes, which also determines the need for frequent replenishment of the anodes; At the same time, the bath works for months without the need to add nickel sulfate.

Wanting to save on nickel, some workshop workers take the line of least resistance and simply apply a thin coating, thereby degrading the quality of the product. The dependence of the mass of deposited nickel on the coating thickness is shown in table. 1.

TABLE 1

THE TIME REQUIRED TO OBTAIN A NICKEL COATING OF A SPECIFIED THICKNESS, S, AND THE MASS OF DEPOSITED NICKEL, mNi, DEPENDING ON THE CURRENT DENSITY. CATHODE CURRENT OUTPUT 92.5%

What is nickel plating?

Nickel plating is a process of treating the outer surface of a metal by applying a layer of nickel to it, which forms a durable protective shell. Most often, the thickness of the nickel layer varies from 1 to 50 microns. There are two methods of nickel deposition process - chemical and galvanic. The galvanic method is used to:

• nickel plating of steel;
• copper;
• aluminum;
• titanium and other metals.

There are also metals that cannot be nickel-plated under any circumstances. These include:

• tin;
• antimony;
• lead;
• cadmium.

In addition, this is a rather complicated procedure, which is strongly recommended not to be done at home, but to seek nickel plating services from professionals.

Preparation of nickel plating baths.

To prepare nickel plating baths, it is recommended to use demineralized water or, in extreme cases, tap water. Ground water should not be used. Working and spare baths made of steel sheet are lined from the inside with hard rubber or polyvinyl chloride. Both baths are thoroughly washed and filled with water, adding sulfuric acid ~5 g/l.

The next day, the baths are thoroughly rinsed and the spare bath is filled halfway with water. The water is heated to 60 °C and with constant stirring, first boric acid is dissolved, then nickel sulfate and nickel chloride.

Since technical chemicals contaminated with foreign metals and organic compounds are usually used to prepare a bath, preliminary cleaning of the bath is necessary. For this purpose, the pH of the bath is increased to 5.0 by introducing freshly precipitated nickel carbonate obtained from nickel sulfate.

In a separate vessel, half filled with warm water, dissolve nickel sulfate and fill it with an aqueous solution of sodium carbonate until the green precipitate of nickel carbonate completely disappears. Carefully drain the water, and add the remaining sediment to the bath in small portions with constant stirring until pH = 5.0. Commercially available basic nickel carbonate is not as good as freshly prepared nickel carbonate because it is less soluble.

Some simplify the process of increasing pH by adding 20% ​​NaOH in small portions to the bath instead of nickel carbonate. The solution must be vigorously stirred for an hour until the green suspension of nickel carbonate is completely dissolved.

After increasing the pH to 5.0, add an aqueous solution of potassium permanganate in small portions with constant stirring until a stable pale pink color appears. Then add activated carbon “Carborol S-extga” (1 g/l) and stir for 2 hours. The bath is left alone until the next day. In this state, the bath should have the natural color of nickel sulfate, but if it does not have this color, then add sulfuric acid to pH = 3.8-4.0; onto the cathode rod until the purple color disappears.

Further cleaning consists of running the baths at low current densities. The solution, previously purified in the spare bath, is pumped into the working bath, adjusted with demineralized water to the specified level, and sulfuric acid is added to pH = 3.8–4.0; the maximum possible number of corrugated steel plates is hung on the cathode rod and a current with a density of initially ~0.5 A/dm2 is turned on, and after several tens of minutes it is reduced to 0.2–0.3 A/dm2. Electrolysis lasts 6 hours with constant stirring and temperature ~ 60 °C. Once the pH is adjusted to normal, the cleaned bath is ready for use. Test loads are nickel-plated in it in order to select optimal processing conditions. For bright nickel plating, appropriate substances are added.

Operation and regeneration of nickel baths. Stabilization of nickel plating baths consists of maintaining specified concentrations of individual components and regulatory removal of contaminants.

It is easiest to adjust the composition based on chemical analysis, but an experienced electroplater can solve these problems independently.

Particular attention should be paid to monitoring and adjusting the pH - a daily responsibility of the personnel responsible for the reliable operation of the nickel bath. Note that this is not very difficult, since the bath gradually becomes alkalized, and, therefore, there is a need to add pure sulfuric acid. Prepare a solution containing 25% (vol/vol) concentrated acid and 75% (vol/vol) distilled water, and add it in small portions to the bath with constant stirring. To control pH, it is enough to have a limited set of indicator paper, for example, three to five ranges produced by PNR.

The color scale on this paper is not as expressive as on Merck papers, but after a certain time the operating personnel will gain experience and will be able to read pH values ​​with sufficient accuracy. Failure to comply with the required pH value will result in a noticeable deterioration in the quality of coatings.

At a very high pH value, i.e. with insufficient acidity, coatings become brittle and prone to peeling, and also acquire a yellow tint; Burning of the coating also easily occurs in places of high current densities. At a pH less than 4, the gloss of the coating is weakened. A nickel bath is easily contaminated with metal impurities, especially when processing brass and zinc products: most often - copper, zinc, iron and lead. Copper gives nickel plating its dark color.

A low concentration of zinc leads to the appearance of black dots on the nickel coating, a high concentration of zinc manifests itself in the form of blackening of the coating in places of low current densities; Heavy zinc contamination can cause black streaks to spread over the entire surface.

Iron contamination leads to an increase in internal stresses in the coating, resulting in the brittleness of nickel. A colloidal suspension of iron compounds appearing in a nickel bath can cause severe pitting.

Lead contamination appears as a brown or silver-brown layer in areas of low current density. Lead can enter the bath from lead pipes used for heating or from immersion heaters placed in a lead casing. This is extremely harmful for baths with shiners.

Impurity metals are removed electrolytically at low current density using the method described when preparing the bath. Cleaning time depends on the degree of contamination of the bath and can last from several hours to several dozen. After a certain time, the steel sheets should be removed from the bath, cleaned with a steel brush and placed back into the bath. You should not leave de-energized sheets in the bath, as this leads to at least partial dissolution of contaminants in it.

Modern nickel plating baths are mixed with air and, therefore, mechanical impurities settling at the bottom are distributed throughout the entire volume of the bath and some of them enter the coating, giving it roughness. Thus, there is a need for continuous filtration of the bath, although most workshops avoid this, limiting themselves to periodic filtration, and do not complain about the roughness of the coatings. This indicates the ability to maintain the bath in proper cleanliness, first of all, the impossibility of getting anode sludge into the bath due to its good retention by the anode bag.

There are different opinions regarding the filtration of bright nickel plating baths using activated carbon. Theoretically, during each bath filtration, carbon should be used to remove harmful organic contaminants, which include, among other things, decomposition products of shine-forming additives. In fact, coal also absorbs some organic additives necessary for normal operation, as a result of which the consumption of rather expensive drugs, for example, “DF-bis” increases.

Despite this unfavorable situation for the consumer, it is necessary to choose a middle ground here, which is that filtration through fresh activated carbon occurs once a week and, finally, the frequency of carbon replacement can be set based on your own observations. Complete abandonment of coal is a technical mistake, since over time the bath becomes so contaminated with organic compounds that the coatings become brittle and passivated, making their decorative chrome plating difficult.

However, it is necessary to pay attention to the type of activated carbon. In Poland, Carbonol S-extga coal is used in dusty form. Random varieties can do more harm than good as they are contaminated with impurity metals such as zinc.

Despite great care of the nickel bath, it can become so contaminated with organic substances that a major regeneration using potassium permanganate becomes necessary.

The contents of the bath, heated to 60 °C, are pumped into a spare bath and the pH is adjusted to 5.5-5.8 using nickel carbonate. Permanganate dissolved in water is added in small portions until a pale pink color is obtained. Thorough mixing is required during the administration of permanganate.

For each liter of bath thus treated, add 3 g of activated carbon and stir vigorously for several hours. Then leave the bath for 10-12 hours, after which the clear solution is carefully filtered into the working bath, without touching the sediment at the bottom. If the pink color remains, then add perhydrol, diluted in distilled water in a ratio of 1:5 until the normal green color of the bath is obtained. To prevent excess perhydrol, it is added in small portions. After adjusting the pH, test products are nickel-plated, remembering that the shine will be worse, since part of the shine-forming solution has been destroyed and only after adding shine-forming agents will the desired decorative appearance be obtained.

Iron contaminating the nickel bath is mainly removed during the low current density treatment described above, however, to more completely remove this metal proceed as follows:

the electrolyte is poured into a spare bath, heated to a temperature of 60 C and alkalized to pH = 6 with nickel carbonate or caustic soda, and stirring is necessary. Then add perhydrol in an amount of 1 cm3/l, stir for 3 hours and leave until the next day. The light solution is carefully filtered into the working bath, making sure that the sediment at the bottom of the bath does not fall into the clean bath.

After bringing the pH to normal, test nickel plating is carried out and glitter-forming additives are added until the desired gloss is obtained.

The correct dosage of brightening agents is the main requirement for success in bright nickel plating. Manufacturers of brighteners give approximate consumption of the substance depending on the amount of electricity passed in ampere hours, but few workshops have electric meters, and recording the load of the bath in the form of detailed records is not as simple as it seems.

During long-term operation of the bath, various situations arise, which are accompanied by a significant loss of brightening agents, for example, during the regeneration of the baths described above. This happens outside of electricity.

The content of the brightener in the bath can be determined analytically, but for this you need to have the appropriate equipment and a thorough knowledge of laboratory techniques. You can use the services of special laboratories, but this is not always possible. Consequently, it remains the own initiative of the galvanizer servicing the bath, or another more competent person.

If we get a semi-shiny coating, this means that there is very little shine-forming agent in the bath. For 100 liters of bath, you can add 25 cm3 of the “DF-bis” additive. If this does not lead to an improvement in shine, then the reason lies in the bath itself. The pH and temperature of the bath should be determined and, if after adjusting these parameters there is still no improvement, then it is necessary to begin cleaning the bath using activated carbon and electrolysis at low current density, which is described in detail when considering baths.

A very difficult situation arises in the case of excessive introduction of brightening agents. In this case, the coatings become brittle in areas of very low current density; for example, in places where the product comes into contact with the pendants, visible black spots form and there may even be final defects in the coatings. Therefore, it is necessary to get rid of excess brightening agent by working the bath under normal conditions, hanging waste steel sheet on the cathode rod, degreasing them accordingly and etching them.

One of the common defects of nickel coatings is porosity - the so-called pitting - small depressions in the coating, reminiscent of pinholes, that occur during nickel plating as a result of the adhesion of hydrogen bubbles to the cathode surface. This is due to the high surface tension, especially in nickel plating baths. A coating does not form at the location of the bubble; a crater appears.

In addition to hydrogen, air bubbles contained in the bath can also settle on the surface of the cathode. The idle bath cools and absorbs a certain amount of air. When the bath is heated, air is released in the form of bubbles, some of which settle on the surface of the cathode, leading to pitting. Before starting nickel plating, the bath should be heated to a temperature several degrees higher than usually used, turn off the heat and wait until the temperature drops to normal. In addition, air may enter the bath due to a leak in the filter pump. Pump leaks should definitely be eliminated.

The condition of the substrate also has a great influence on the formation of pitting, the porosity of which, non-metallic inclusions and all kinds of surface contamination contribute to the formation of pitting. Contamination of the bathtub with suspension or decay products of organic substances also affects the bathtub in the same way.

To prevent the formation of pitting, oxidizing or wetting agents are added to the bath. The first includes hydrogen peroxide, added to ordinary baths in the form of perhydrol in quantities of 0.2-0.5 cm3/l.

Perhydrol is not added to baths with shine formers, as it has a destructive effect on organic substances. In such cases, wetting agents, for example, sodium lauryl sulfate, are added in an amount of 0.1-0.2 g/l.

Hydrogen peroxide and wetting agent are not radical anti-pitting agents. Mechanical shaking of products on suspensions in the bath helps eliminate gas bubbles. A movable cathode rod, or even better, mixing the bath with compressed air, makes the fight against pitting much easier. For persistent pitting, bath cleaning with activated carbon should be used.

STATE STANDARD OF THE USSR UNION

Introduction date for newly developed products is 01/01/87

for products in production - when revising technical documentation

This standard specifies the designations of metallic and non-metallic inorganic coatings in technical documentation.

1. Designations of base metal processing methods are given in table. 1.

Table 1

2. Designations of methods for obtaining coating are given in table. 2.

table 2

* The method of producing coatings colored during the anodic oxidation of aluminum and its alloys, magnesium and its alloys, titanium alloys is designated “Anocolor”.

** The method of producing coatings by thermal decomposition of organometallic compounds is designated Mos Tr

Table 2
(Changed edition, Amendment No. 3).
3. The coating material, consisting of metal, is designated by symbols in the form of one or two letters included in the Russian name of the corresponding metal.

The designations of the coating material, consisting of metal, are given in table. 3.

Table 3

4. Designations of nickel and chrome coatings are given in mandatory Appendix 1.

5. The coating material, consisting of an alloy, is designated by the symbols of the components included in the alloy, separated by a hyphen, and the maximum mass fraction of the first or second (in the case of a three-component alloy) components in the alloy is indicated in parentheses, separating them with a semicolon. For example, coating with a copper-zinc alloy with a mass fraction of copper 50-60% and zinc 40-50% is designated M-C (60); coating with a copper-tin-lead alloy with a mass fraction of copper 70-78%, tin 10-18%, lead 4-20% is designated M-O-C (78; 18).

In the designation of the alloy coating material, if necessary, it is allowed to indicate the minimum and maximum mass fractions of the components, for example, coating with a gold-nickel alloy with a mass fraction of gold of 93.0-95.0%, nickel of 5.0-7.0% is designated Zl-N ( 93.0-95.0).

When designating the coating of watch and jewelry parts with alloys based on precious metals, it is allowed to indicate the average mass fraction of the components.

For newly developed alloys, the components are designated in order of decreasing their mass fraction.

(Changed edition, Amendment No. 2).

6. Designations of alloy coatings are given in table. 4.

Table 4

Table 4
(Changed edition, Amendment No. 3).
7. In the designation of the coating material obtained by burning in, indicate the brand of the starting material (paste) in accordance with the regulatory and technical documentation.

8. In the designation of solder coating obtained by the hot method, indicate the brand of solder in accordance with GOST 21930-76, GOST 21931-76.

9. Designations of non-metallic inorganic coatings are given in table. 5.

Table 5

10. If it is necessary to indicate the electrolyte (solution) from which the coating is to be obtained, use the designations given in the mandatory appendices.

Electrolytes (solutions) not listed in the appendices are designated by their full name, for example, Ts9. ammonium chloride. xp, M15. pyrophosphate.

11. Designations of the functional properties of coatings are given in table. 6.

Table 6

12. Designations of decorative properties of coatings are given in table. 7.

Table 7

* The color of the coating corresponding to the natural color of the deposited metal (zinc, copper, chromium, gold, etc.) does not serve as a basis for classifying the coating as painted.

The color of the coating is indicated by its full name, with the exception of black coating – part.

13. Designations for additional coating processing are given in table. 8.

Table 8

* If necessary, indicate the color of the chromate film: khaki - khaki, colorless - btsv; rainbow film color – no designation.

14. The designation of additional treatment of the coating by impregnation, hydrophobization, or application of paint and varnish coating may be replaced by the designation of the brand of material used for additional processing.

The grade of material used for additional coating processing is designated in accordance with the regulatory and technical documentation for the material.

The designation of a specific paint coating used as an additional treatment is carried out in accordance with GOST 9.032-74.

15. Methods of preparation, coating material, designation of electrolyte (solution), properties and color of the coating, additional processing not listed in this standard are indicated according to the technical documentation or written down by the full name.

(Changed edition, Amendment No. 2).

16. The procedure for designating the coating in technical documentation:

designation of the method of processing the base metal (if necessary);

designation of the method of obtaining the coating;

designation of coating material;

minimum coating thickness;

designation of the electrolyte (solution) from which the coating is required (if necessary);

designation of functional or decorative properties of the coating (if necessary);

designation of additional processing (if necessary).

The designation of the coating does not necessarily contain all of the listed components.

If necessary, it is allowed to indicate the minimum and maximum thicknesses separated by a hyphen in the designation of the coating.

It is allowed to indicate the production method, material and thickness of the coating in the designation of the coating, while the remaining components of the designation are indicated in the technical requirements of the drawing.

(Changed edition, Amendment No. 2).

17. Coating thickness equal to or less than 1 micron is not indicated in the designation unless there is a technical need (except for precious metals).

18. Coatings used as technological coatings (for example, zinc during zincate processing of aluminum and its alloys, nickel on corrosion-resistant steel, copper on copper alloys, copper on steel made from cyanide electrolyte before acid copper plating) may not be indicated in the designation.

19. If the coating is subjected to several types of additional processing, they are indicated in technological sequence.

20. The coating designation is recorded on a line. All components of the designation are separated from each other by dots, with the exception of the coating material and thickness, as well as the designation of additional paint coating treatment, which is separated from the designation of a metallic or non-metallic inorganic coating by a fraction line.

The designation of the production method and coating material should be written in capital letters, the remaining components - in lowercase letters.

Examples of recording the designation of coatings are given in Appendix 4.

(Changed edition, Amendment No. 1, 2, 3).

21. The procedure for designating coatings according to international standards is given in Appendix 5.

21. Introduced additionally (Changed edition, Amendment No. 3).

Mandatory

DESIGNATIONS FOR NICKEL AND CHROME COATINGS

* If necessary, the technical requirements of the drawing indicate the symbol of the chemical element or the formula of the chemical compound used as the precipitated substance.

Note. It is allowed to use abbreviations and indicate the total thickness of the coating.

(Changed edition, Amendment No. 2).

Mandatory

DESIGNATIONS OF ELECTROLYTES FOR OBTAINING COATINGS

Mandatory

DESIGNATIONS FOR SOLUTIONS FOR OBTAINING COATINGS

(Changed edition, Amendment No. 1).

Mandatory

EXAMPLES OF RECORDING COATING DESIGNATIONS

Information

DESIGNATION OF COATINGS ACCORDING TO INTERNATIONAL STANDARDS

1. The base metal and coating material is designated by the chemical symbol of the element.

The base metal material, which consists of an alloy, is designated by the chemical symbol of the element with the highest mass fraction. The main non-metallic material is designated NM, plastic – PL.

The coating material, consisting of an alloy, is designated by the chemical symbols of the components included in the alloy, separating them with a hyphen. The maximum mass fraction of the first component is indicated after the chemical symbol of the first component before the hyphen.

2. The designation of methods for obtaining the coating is given in table. 9.

Table 9

3. Designations for additional coating processing are given in table. 10.

Table 10

* The color of the chromate film is indicated by:

A – colorless with a bluish tint; B – colorless with a rainbow tint; C – yellow, rainbow; D – olive (khaki).

Coatings A and B belong to the 1st class of chromate coatings, coatings C and D, which have higher corrosion resistance, belong to the 2nd class.

4. The designation of types of nickel and chromium coatings is given in table. eleven.

Table 11

5. The designation is written on the line in the following order:

the chemical symbol for the base metal or the symbol for the nonmetal followed by a slash;

method of coating, in which the chemical symbol of the metal of the sublayer is indicated;

chemical symbol of the coating metal (if necessary, the purity of the metal in percentage is indicated in parentheses);

a figure expressing the minimum thickness of the coating on the working surface in microns;

designation of the type of coating (if necessary);

designation of additional processing and class (if necessary).

Examples of designations are given in table. 12.

Table 12

Appendix 5 Added additionally (Change No. 3).

INFORMATION DATA

1. DEVELOPED AND INTRODUCED by the Academy of the Lithuanian SSR

DEVELOPERS

E.B. Davidavichus

, Ph.D.
chem. sciences; G.V.
Kozlova , Ph.D.
tech. sciences (topic leaders); E.B.
Romashkene , Ph.D.
chem. sciences; T.I.
Berezhnyak ;
A.I.
Volkov , Ph.D.
tech. sciences; T.A.
Karmanova 2. APPROVED AND ENTERED INTO EFFECT by Resolution of the USSR State Committee on Standards dated January 24, 1985 No. 164

3. The date of the first inspection is 1992; inspection frequency – 5 years

4. Instead of GOST 9.037-77; GOST 21484-76

5. REFERENCE REGULATIVE AND TECHNICAL DOCUMENTS

6. REISSUE with Amendments No. 1, 2, approved in October 1985, February 1987 (IUS 1-86, 5-87)

Change No. 3 was made, approved by Resolution of the State Standard of Russia dated May 22, 1992 No. 498 (IUS 8-92)

Nickel anodes

Nickel anodes are manufactured in accordance with the PN-82/N-92914 standard with dimensions of 25x25x(3-8) mm and sheets 100-300 mm wide, 600-1000 mm long and 6-12 mm thick.

The chemical composition of the anodes must comply with the PN-79/N-8181 standard, and the sheets - with the PN-79/82180 standard. Anodes in the form of sheets have grades No. 2, No. 3 and No. 6A. For bright nickel plating, anodes No. 2 are used. An example of anode designation when placing an order: nickel anode No. 2 8Х300Х600 in accordance with standard RN-82/N-92914. The cubes are placed in titanium baskets.

Removing Nickel Platings

Nickel coatings on steel and copper alloys are typically removed in a dilute sulfuric acid bath. To 20 liters of cold water, add 30 liters of concentrated sulfuric acid in portions with constant stirring, making sure that the temperature does not exceed 60 ° C. After cooling the bath to room temperature, its density should be ~1.63.

In order to reduce the risk of seeding of the substrate material, 50 g/l glycerol is added to the bath. Bathtubs are made of vinyl plastic. The products are hung on the middle rod connected to the positive pole of the current source. The side rods, on which lead sheets are hung, are connected to the negative pole of the current source. The bath temperature should not exceed 30 °C, since the hot solution acts aggressively on the substrate. The current density reaches 4 A/dm2, but the voltage can be varied within 5-6 V. After a certain time, concentrated sulfuric acid should be added to maintain a density of 1.63. In order to prevent dilution of the bath, it is necessary to immerse the products in the bath after pre-drying them. In the case of brass products, controlling the process is not difficult, since at the moment of complete removal of nickel, the current density drops sharply.

Black Nickel Platings

Black nickel coatings are used for decorative and special purposes. Their protective properties are very low, so they are applied to an underlayer of zinc, cadmium or ordinary nickel. Steel products are pre-galvanized, and brass and copper are nickel-plated.

Black nickel plating is hard and brittle, especially when thick. In practice, a thickness of 2 microns is usually satisfied. The bath for applying such coatings contains a significant amount of zinc and thiocyanate. The coating contains ~50% nickel, with the rest being zinc, sulfur, nitrogen and carbon. Below are typical compositions of black nickel plating baths, g/l:

Electroless nickel plating

This process was at one time one of the main ones in the technical literature, and it seemed that it created strong competition for traditional electrolytic nickel plating. Currently, it is assessed more calmly and used when there is technical and material support for this.

The main advantage of electrochemically applied nickel coatings is the uniform thickness regardless of the shape of the product. This is typical for all metal deposition processes without the use of current.

A feature of chemical nickel plating is the continuous deposition of a layer, which creates the possibility of forming coatings of any thickness.

Baths for chemical nickel plating consist of nickel salt, sodium hypophosphite and additives. The basis is nickel salts and sodium hypophosphite.

There are two types of baths for chemical nickel plating - acidic and alkaline. Nickel sulfate or chloride of relatively low (~5 g/l) concentration is mainly used as nickel salts. The content of hypophosphite reaches 10-30 g/l. Additives are introduced in the form of complexing compounds that accelerate the deposition of nickel, and stabilizers that prevent the decomposition of the electrolyte.

Glycolic, lactic, citric and aminoacetic acids are mentioned as complexing compounds in the specialized literature. Accelerators are succinic, malonic, propionic, butyric, valeric and other acids. Lead compounds, thiosulfate, thiourea, etc. are mainly used for stabilization.

Below are examples of two baths for electroless nickel plating, g/l: