Steel 20; quality, characteristics, range, scope of application and operating conditions

The alloy, which is characterized by ease of use, ease of processing, good strength and hardness, as well as low cost, can confidently be called universal, applicable in any conditions. Steel 20 is not a specialized steel; on the contrary, its application possibilities are so wide that it has found a place in almost every industrial sector.

Detailed information on the supply of sheet steel and a price calculator can be found on our website.

Total information

Steel 20 is a structural carbon quality steel widely used in industry. Its popularity is not inferior to 09G2S steel, although in terms of technical and operational characteristics there is a noticeable difference between these grades. Steel 20 is used mainly for the production of parts, welded structures, in construction, and mechanical engineering, but a complete list of industries for its use would take several pages of text. The practicality of steel of this grade allows it to occupy one of the leading positions on the market among ferrous rolled metals.

Alloy influence

The next aspect that influences how seamless steel pipes will be used is the steel grade. Possible types of alloys are indicated in the above-mentioned state standards. In particular, the following steels are used for the production of hot-rolled steel:

• carbon of normal quality,
• high-quality construction,
• alloyed structural,
• increased strength.

For the production of cold-deformed products, the first type from the list is not used, but an additional type is used - spring-carbon and alloy.

As for specific grades, the following steels are used according to the standard for hot-rolled steel: st2sp, st4sp, st5sp, st6sp, 10, 20, 35, 45, 10G2, 20Х, 40Х, 30ХГСА, 15ХМ, 30ХМА, 12ХН2, 09Г2С and others.

Seamless steel pipe made from alloys St10-45 and 09G2S can be considered the most popular on the market.

Cold-deformed pipes according to GOST are produced from a smaller number of grades due to the fact that not all of them allow effective deformation without increasing the temperature. These include: st10-45, 09G2S, 10G2, 15Х, 20Х, 40Х, 30ХГСА, 15ХМ.

Products from grades 10, 20 and 09G2S are in high demand.

Characteristics

The metal is characterized by excellent weldability; there are no special requirements for welding, except in cases where the parts have previously been subjected to chemical or heat treatment. Steel 20 is not prone to temper brittleness and is insensitive to flakes and flake sensitivity. The alloy is resistant to pressure treatment, can be cut well by any means, does not crack, and is amenable to surface machining.

Steel 20 is less resistant to chemical attack; contact with alkalis and acids is not recommended. There is no protection against corrosion; products made from steel 20 are not recommended for use in conditions of high humidity, in contact with water without additional protective coatings (zinc, chrome or paint).

Characteristics of steel 20

High-quality steel 20 must meet standards, have certain parameters and scope of use. Let's consider due to what characteristics the alloy remains in demand and popular.

Since steel grade 20 is a high-quality material, strict requirements are imposed on its chemical composition. Smelting is carried out according to the rules prescribed in GOST steel 20. The composition includes the following components:

• Iron (Fe) – approximately 98%.
• Carbon (C) – 0.2%. The number 20 in the name indicates the content of this element. Carbon is responsible for strength. The more it is, the harder and more durable the alloy becomes.
• Silicon (Si) – 0.17-0.35%. Needed to remove hydrogen, oxygen, nitrogen from the composition. They increase porosity and the number of gas pockets, which significantly reduce the strength of the metal.
• Manganese (Mn) – 0.35-0.65%. Also a serious deoxidizer, it also promotes the removal of sulfur. Improves surface quality, reduces the risk of cracks during hot working. Thanks to it, welding and forging proceed better.
• Nickel (Ni) – up to 0.3%, chromium (Cr) – up to 0.2%, copper (Cu) – up to 0.3%. The elements lead to improved mechanical and corrosion-resistant properties. However, since their number is small, they do not have a serious effect on the steel.
• Phosphorus (P) – up to 0.035%, sulfur (S) – up to 0.04. Harmful impurities. If their content is too high, the steel becomes too brittle. In addition, the viscosity index drops.

Deoxidation level

• Calm steel 20. Due to the introduction of silicon and manganese, oxygen is completely absent. Iron oxides are also in very small quantities. This ensures “quiet” solidification of the metal in the ladle. The homogeneity and density of ST20 at the outlet are excellent, only a gas shell is formed on top.
• Boiling steel. It is formed by the deoxidation of manganese, which leads to an increase in the content of ferrous oxide. The compound forms carbon dioxide. As a result, gas bubbles form, looking like a boiling mass. Such a metal is very porous, chemical elements are distributed unevenly, which causes deterioration in mechanical characteristics, increases the risk of cracks, and impairs weldability. But there are also advantages - low price, absence of unsafe waste.
• Semi-quiet ST20. Something in between the previous varieties of the alloy.

Types of processing

• forged,
• calibrated,
• hot rolled,
• silver (it has a round base and is coated with a special composition).

The density of steel is 20 - 7850 kilograms per cubic meter. The melting point is 1500 degrees Celsius. The mixture becomes completely liquid at a temperature of 1600 °C. The alloy gives off heat easily, but also accumulates it well. Thermal conductivity coefficient is 48 W/(m deg), specific heat capacity is 490 J/(kg °C). Steel conducts current very well.

The material has low chemical resistance to most acidic compounds. If moisture gets on the surface, rust will remain on it. Because of it, the appearance and strength are greatly deteriorated.

To protect the material from corrosion, galvanic coatings (chrome, zinc, and other similar compounds) should be applied.

The steel is highly plastic, the strength is average, and the hardness is good. The elastic modulus is 200 MPa. The rupture occurs when the greatest elongation is reached at 23-26%, the relative narrowing is even greater - 55%.

Strength indicators are increased by peening, possibly rolling with rollers. Normalization or hardening annealing is performed. In this case we mean the thermal method of exposure.

It is characterized by increased viscosity; accordingly, the alloy is able to withstand impacts. Impact strength – 780 kJ/m².

It lends itself perfectly to pressure treatment and withstands any type of cutting. Stamping is mainly carried out hot. Does not crack during steam treatment and under high pressure. Weldability group 1.

• ST20 is included in the subgroup of cemented alloys. The hardness of the cemented layer is up to 62 HRC, while the core remains “soft”, in the range of 20-35 HRC.
• Chemical exposure and heat treatment (hardening) strengthen the metal and increase its service life.
• Weldability without restrictions, is not characterized by flake sensitivity, and is not prone to temper brittleness.

Advantages and disadvantages of steel 20

Steel 20 is distinguished by its quality and relatively low production cost. It is an upgradeable alloy, making it adaptable to a wide range of conditions and, as a result, widespread.

Steel 20 is corrosion-resistant and susceptible to chemical influences - this is its main drawback. The advantages include:

• good weldability without special requirements for the procedure;
• disinclination to temper fragility;
• insensitivity to flakes;
• price-quality ratio;
• material density;
• moderate strength.

Steel 20 is a ferrous metal with a simple composition without expensive alloying additives. The alloy has been produced for a long time, the production process is well studied, optimized, and worked out; There are no special conditions or requirements, so the metal is not very expensive.

Steel 20. Characteristics and analogues – All about steel

Grade 20 steel has been used for many years in virtually every industry. Its widespread use is due to its mechanical and physical properties, relative simplicity and low cost of production.

Application

Grade 20 steel is most widely used in the manufacture of various sections of pipes, and also occupies the largest niche in mechanical engineering for the manufacture of parts with low loads. Widely used for structures operating at temperature or under pressure - boilers, manifolds, pipelines.

The boundaries of use of steel 20 can be expanded using the so-called chemical-thermal heat treatment. The most common processes used for this steel are carburization, nitrocarburization or cyanidation. Strengthening occurs through saturation with carbon or a mixture of carbon and nitrogen. After such heat treatment, the surface hardness and wear resistance of the steel increases to a small depth, the core of the material remains relatively soft. In this case, parts made of steel 20 work in the most critical or key components of the mechanisms. In this way, gears, satellites, and other worm gears with a high service life and wear resistance of the surface layer of the teeth are manufactured.

Quantitative composition

The qualitative and quantitative composition of steel 20 includes both fundamental elements for all steels and impurities in small quantities and concentrations. The main components of this steel are iron about 98%, carbon from 0.17 to 0.24%, silicon from 0.17 to 0.37%, manganese from 0.35 to 0.65%, nickel and copper no more 0.25%. This steel may also contain sulfur and phosphorus in an amount of no more than 0.04%.

Analogs

Analogues of steel 20 in chemical composition and physical properties are steels 15 and 25. They have a similar structure and quality when used, differing only in the percentage of carbon content.

According to the steel grade, substitutes for steel 20 can also be grades 15HFA, 20F, 09SFA.

Steel grades 20L and 20X have a similar quantitative carbon content; they have slightly different areas of application. Steel 20L is used for castings, steel 20X is chromium-alloyed steel (contains up to 1% chromium). These steels have similar technological properties to steel 20.

Types of production

Steel 20 is supplied in the form of sheets, various pipes, calibrated rods, castings and other profiles. Also, products made from this steel can be without heat treatment and normalized.

Characteristics

1. The hardness of steel 20 material in a heat-treated state, after annealing, should be 167 HB, of calibrated cold-worked material 207 HB.
2. Steel lends itself well to forging and stamping, the forging temperature at the beginning should be 1280 C, at the end about 750 C, cooling in air.
3. After heat treatment, steel is not subject to the phenomenon of temper brittleness.
4. This steel does not have a tendency to temper brittleness.
5. Steel without heat treatment and in a normalized state can be welded without any restrictions (not after surface hardening).
6. Corrosion resistant steel compared to other low carbon structural steels.

Structures and parts made from grade 20 steel have a fairly long service life, are inexpensive materials, quickly pay for themselves, and have a number of other performance properties. To produce the necessary parts, blanks of this steel are available in a wide selection; for some purposes, circles or wire are used, for others pipes are important, and still others are selected from forgings or sheets.

specural.com

Explanation of markings

The marking of steel 20 indicates the chemical composition of the alloy, in particular; on the proportion of carbon in the composition. Since 20 steel is considered high quality, higher demands are placed on the accuracy of its chemical composition.

Chemical composition

The chemical composition of steel 20 includes the following elements and their designations:

• Carbon. The first digit 20 indicates the carbon content in hundredths, i.e. 0.2%. The advantage of steel with a high carbon content is higher strength, but this same indicator leads to a decrease in ductility.
• Silicon. The proportion of silicon in the alloy ranges from 0.17 to 0.35%. Due to the presence of silicon in the metal composition, porosity and the number of gas pockets, which negatively affect the strength of the alloy, are reduced. Pores and cavities are formed due to oxygen, nitrogen and hydrogen gases, the particles of which are removed by silicon.
• Manganese. The proportion of manganese ranges from 0.35 to 0.6%. Manganese, like silicon, prevents oxidation and also removes sulfur from the composition. Thanks to manganese, heat treatment under pressure occurs with a low probability of crack formation, the effectiveness of forging and welding works improves, and the surface of products becomes of higher quality.
• Chrome, copper, nickel. The proportion of nickel and copper usually does not exceed 0.3%, the proportion of chromium; 0.2%. These are alloying additives that have a positive effect on the properties of steel, but in this case their content is insignificant, so they do not have a noticeable effect on the characteristics of the alloy.
• Phosphorus, sulfur. Phosphorus content is permissible up to 0.035%, sulfur; up to 0.04%. These are impurities that have a harmful effect on steel. They increase brittleness and negatively affect toughness, as a result of which the steel loses its resistance to dynamic loads.
• Iron. The rest of the alloy is iron.

Chemical composition in % of material 20

GOST 1050-88

Chemical composition

Fe is the basis. According to TU 14-1-1672-76, the chemical composition is given for steel grade 20A. The residual copper content is allowed no more than 0.25% when steel is smelted using the scrap process. Deviations from the norms of chemical composition are allowed in accordance with GOST 1050. Upon request, steel can be supplied with narrowed carbon content limits - “select”: 0.19-0.25%; 0.19-0.23%; 0.22-0.25%; 0.21-0.24%. According to GOST 1050-88, the nitrogen content is indicated for steel using the oxygen-converter smelting method. For all other types of steelmaking, the nitrogen content is N≤0.008%. According to TU 14-1-5185-93, TU 14-1-5058-91, the chemical composition is given for steel grade 20pv. According to TU 08.002.0501.5348-92, the chemical composition is given for steel grade 20-Sh. According to TU 14-1-3987-85, the chemical composition is given for steel grade 20. According to TU 14-1-1529-2003, TU 14-3-460-2003 and TU 14-3-341-75 for steel made from scrap process or from cuprous ores, the mass fraction of residual copper and nickel is allowed up to 0.30% each. The technological addition of rare earth elements is allowed to improve the quality of the metal. According to TU 14-3R-55-2001, the chemical composition is given for steel 20; for steel 20-PV, the mass fraction of carbon is 0.18-0.24%, chromium, nickel, copper, sulfur and phosphorus ≤ 0.15% each, the mass fraction of other elements is identical to steel grade 20. In steel 20, nickel and chromium no more than 0.40% each. The presence of rare earth elements introduced as technological additives is allowed. According to GOST 19277-73, GOST 21729-76, the chemical composition is given for steel 20A. When smelting steel using the scap process, the mass fraction of copper should be ≤ 0.25%. Maximum deviations for the chemical composition are in accordance with GOST 1050. According to TU 1317-006.1-593377520-2003, the chemical composition is given for steel grade 20A. The mass fraction of hydrogen in steel in the pipe metal should not exceed 1.0 ppm (2.0 ppm in the ladle sample. It is allowed to introduce niobium and titanium to obtain a mass fraction of up to 0.030% and 0.010%, respectively. In deoxidized steel for globularization of sulfide inclusions calcium (silicocalcium) or cerium is introduced to obtain a mass fraction of 0.050%. According to TU 14-162-14-96, the chemical composition is given for steel grade 20A. Deviations in the content of carbon (-0.020%), aluminum (±0.010%) are allowed in steel ), manganese (+0.15%), sulfur (+0.005%), phosphorus (+0.005%). In order to increase strength properties, it is allowed to introduce vanadium into steel in an amount of up to 0.050%. According to TU 14-3-1971-97 The chemical composition is given for steel grade 20B with increased corrosion resistance and operational reliability. To ensure a fine-grained structure, vanadium is introduced up to 0.06%. The carbon equivalent SEq should not exceed 0.40%. According to TU 1301-039-00212179-2010, the chemical composition is given for steel grade 20-Sh. The content of each impurity element not regulated by the table is allowed up to 0.050%. According to TU 108.1273-84, deviations for nickel are +0.20%, for copper +0.20%. According to TU 14-158-113-99, the chemical composition is given for steel grade 20 with increased corrosion resistance and cold resistance. In the finished metal, deviations in chemical composition are allowed in accordance with GOST 1050, in addition - for aluminum + 0.0050%. When the mass fraction of nitrogen is more than 0.0080%, microalloying with vanadium of at least 0.030% is mandatory. According to TU 14-161-149-94, the chemical composition is given for steel grade 20 for hydrogen sulfide- and cold-resistant casing pipes and couplings.

Types of rental

There are two main technologies for producing rolled profiles from steel 20:

1. Hot deformation - used for rolling workpieces more than 4 mm thick. Hot deformation leads to the formation of scale, which is the main disadvantage of this technology.
2. Cold deformation; used for rolling thin workpieces (up to 4 mm). As a result of cold deformation, the strength of the alloy increases due to cold hardening.

Types of steel products 20

• profile of all varieties: channel, sheet, I-beam, angle, rod, wire;
• seamless, high-strength pipes obtained by drawing (cold or hot);
• all-welded cold-rolled pipes, welded from a single sheet of steel 20 along the length of the pipe.

Production Standards

• long products, including shaped steel - GOST 1050-88, GOST 2590-2006, GOST 2591-2006, GOST 2879-2006, GOST 8509-93, GOST 8510-86, GOST 8240-97, GOST 8239-89;
• calibrated rod - GOST 7417-75, GOST 8559-75, GOST 8560-78, GOST 10702-78;
• polished rod and silver - GOST 14955-77;
• thick sheet - GOST 1577-93, GOST 19903-74;
• thin sheet - GOST 16523-97;
• tape - GOST 6009-74, GOST 10234-77, GOST 103-2006, GOST 82-70;
• wire - GOST 5663-79, GOST 17305-91;
• forgings and forged blanks - GOST 8479-70;
• pipes - GOST 10704-91, GOST 10705-80, GOST 8731-74, GOST 8732-78, GOST 8733-74, GOST 5654-76, GOST 550-75.

Purpose and application

Steel 20 is one of the most common steel grades in the domestic industry; its versatility allows the production of almost all types of metal products. The main areas of application of steel 20:

1. Mechanical engineering. Steel 20 is used to make fastening devices, connecting elements of mechanisms, gears, worms, brackets, bearing shafts, and liners.
2. Pipelines. Steel 20 is used to make welded and seamless pipes, shut-off valves and adapters; crosspieces, union nuts, nipples, fittings, hexagons, couplings, taps, manifolds, superheaters, parts of boilers operating under high pressure.
3. Construction. Fasteners, hooks, load-bearing trusses, beams and much more. In construction, steel 20 is popular due to its good weldability, satisfactory strength and availability.

Structural quality carbon steel 20

Structural high-quality carbon steel is used for the production of hot-rolled sheets, circles, strips, seamless pipes, electric-welded pipes, hexagons, manifolds, pipelines, superheaters, other parts of high-pressure boilers, sheets for stamping, cemented products with a long service life at temperatures up to +3500C.

Steel 20 is one of the most practical steel grades, widely used for the production of steel pipes and hot-rolled sheets.

Metal grade Substitute

Three types of steel 20 according to deoxidation level

Deoxidation is the removal of oxygen from the composition of steel 20 in order to reduce the brittleness during hot working. The degree or level of deoxidation can also be called the degree of gas evolution during steel solidification. The intensity of gas evolution or boiling greatly affects the structure of the frozen metal; accordingly, the higher the level of deoxidation, the more solid and durable the structure will be.

Quiet and semi-quiet steel

Steel, which is deoxidized by silicon and manganese, can be maximally purified of oxygen content. Such steel is characterized by a complete structure without bubbles and pores, because the alloy solidifies in a calm state, without active release of gases. The formation of a shrinkage cavity occurs in the upper part; it is removed mechanically.

Quiet steel is more expensive than boiling and semi-quiet steel, because more difficult to produce. It is used in the manufacture of products with high strength requirements, for example, for load-bearing structures, railway tracks, etc.

Semi-quiet steel; an average state between calm and boiling steel, characterized by medium porosity. It comes in different qualities and is used for the manufacture of welded structures, blanks for rolled pipes, and fasteners.

Calm steel has the highest levels of strength and reliability, but its use may not be economically viable in industries where high demands are not placed on steel products.

Boiling steel

Steel 20, the deoxidation process of which is carried out thanks to manganese, contains the largest amount of dissolved gases and iron oxides. When boiling steel hardens, nitrogen and carbon dioxide are actively released, and multiple bubbles and pores are formed. Such steel is inferior to calm and semi-quiet steel in terms of strength, but has a number of positive characteristics. It is perfectly stamped, the process of its production is simpler and cheaper, and the production is waste-free.

Boiling steel is suitable for the production of products that are not subject to high loads during operation. This can be various types of fencing, sheet cladding, and other metal structures.

Steel grades

Steel 20 characteristics.

According to the classification, steel 20 refers to structural steel, or more precisely, steel 20 is high-quality carbon structural steel. Steel 20 is used in a wide variety of designs, both general and special purpose. Steel 20 is used for the manufacture of: superheater pipes, manifolds and pipelines of high-pressure boilers, sheet steel 20 is used for stamped parts, and steel 20 is also used to make cemented parts for long and very long service at temperatures up to 350°C. Steel 20 is intended for - after normalization or without heat treatment, crane hooks, couplings, bearing shells and other parts operating at temperatures from 40 degrees to 450 under pressure. After CHT (chemical-technical processing), steel 20 can be used for the manufacture of: gears, worms and other parts that require high surface hardness with a relatively low core strength of the parts. Substitute: St15, St25. Weldable without restrictions, except for parts after chemical-thermal treatment.

Steel 08Х18Н10Т characteristics.

Steel 08Х18Н10Т is corrosion-resistant, heat-resistant, one of the most common grades of stainless high-alloy steels. Widely used for the production of steel flanges 08Х18Н10Т, in valve engineering, and for the production of heat exchange equipment. Flanges made of steel 08Х18Н10Т work in highly aggressive working environments. It has stainless properties, which are due to the presence of chromium-nickel group of chemical elements. The second name is “technical stainless steel”. It differs from steel 12Х18Н10Т, it has a lower carbon content (by 4%). Below are the main properties and characteristics of steel 08Х18Н10Т. Application: welded equipment operating in highly aggressive environments, heat exchangers, muffles, pipes, furnace fittings, spark plug electrodes; Austenitic steel. Weldable without restrictions.

Steel 12Х18Н10Т characteristics.

Steel 12Х18Н10Т-structural cryogenic steel/corrosion-resistant ordinary steel, belongs to the austenitic class. After standard heat treatment, consisting of hardening at 1050 0C with cooling in water, the steel has a solution structure. Steel 12Х18Н10Т does not undergo any transformations when heated to hot plastic deformation and when cooled to -196* C. With long exposures in the range of 450 – 650 0C, the release of chromium carbides of the Cr23C6 type is observed, which causes the steel to become prone to intergranular corrosion with minimal incubation period at 600 0C and equal to 8 - 10 hours (test in boiling 65% nitric acid, three cycles of 48 hours). Application: parts operating up to 600 °C. Welding apparatus and vessels operating in dilute solutions of nitric, acetic, phosphoric acids, solutions of alkalis and salts and other parts operating under pressure at temperatures from -196 to +600 °C, and in the presence of aggressive media up to +350 °C; austenitic class steel. Replacement: steel 08Х18Г8Н2Т, steel 10Х14Г14Н4Т, steel 12Х17Г9А4, steel 08Х22Н6Т, steel 08Х17Т, steel 15Х25Т, steel 12Х18Н9ТС can be welded without restrictions.

Steel 09G2S characteristics.

Steel 09g2s belongs to low-alloy steels, the total amount of alloying additives in which does not exceed 2.5% (in contrast to high-alloy steels, where this figure is over 10%). Steel 09g2s can be replaced with the following grades: 09g2, 09g2dt, 09g2t, 10g2s, and also 19Mn-6. Application: various parts and elements of welded metal structures operating at temperatures from -70 to +425°C under pressure. Welding is possible both when heated to 100-120°C, with subsequent heat treatment, and without heating and treatment. Good weldability of steel is ensured due to its low (less than 0.25%) carbon content. If there is more carbon, then micropores may form in the weld when carbon burns out and hardening structures may appear, which deteriorates the quality of the seam. Another advantage of this grade is that 09g2s steel is not prone to temper brittleness, that is, its toughness does not decrease after the tempering procedure. It is also resistant to overheating and cracking. Replacement: 09G2, 09G2DT, 09G2T, 10G2S.

Steel St3sp (VSt3sp) characteristics.

Steel St3sp is a structural carbon steel of ordinary quality. Application: Load-bearing and non-load-bearing elements of welded and non-welded structures and parts operating at positive temperatures. Shaped and sheet metal (5th category) with a thickness of up to 10 mm for load-bearing elements of welded structures operating under variable loads in the range from – 40 to +425 degrees Celsius for St3ps and a thickness of up to 25 mm. For St3sp, St3ps with rolled thickness from 10 to 25mm. – for load-bearing elements of welded structures operating at temperatures from -40 to + 425 degrees, subject to delivery with guaranteed weldability, St3sp with rolled metal thickness over 25 mm – for load-bearing elements of welded structures operating at temperatures from -40 to + 425 degrees Celsius , subject to delivery with guaranteed weldability. Weldability: without restrictions - welding is carried out without heating and without subsequent heat treatment; limited weldability - welding is possible when heated to 100-120 degrees. and subsequent heat treatment, difficult to weld - to obtain high-quality welded joints, additional operations are required: heating to 200-300 degrees. during welding, heat treatment after welding - annealing.

aa61.ru

Mechanical properties

Steel 20 is characterized by high mechanical properties, such as ductility, hardness and strength. The high impact strength allows the steel to adequately withstand increased dynamic loads. Strength is improved by thermal or mechanical treatments - peening, roller rolling, annealing, normalization.

The specific gravity of steel is 7.85 g/cm3. Maximum linear expansion coefficient st 20 = 14.8·10-6 deg-1 at temperatures 27-700°C. Indicators for calibrated hot-rolled steel of the 2nd category: temporary tensile strength 410 MPa, relative elongation after fracture 25%, relative contraction 55%, Brinell hardness 4.8.

Mechanical properties at T=20oC of the material 20.

Mechanical properties of steel 20 at elevated temperatures 0С

Steel endurance limits 20

Mechanical properties of steel 20 after chemical treatment

Composition of steel grade 20

The chemical composition of steel 20 is regulated by GOST 1050-58. According to his requirements, the mass fraction of carbon in the ladle sample of the alloy should be from 0.17% to 0.24%. Therefore, steel 20 is classified as low-carbon.

Standards for the content of other chemical elements in it according to GOST:

• nickel and copper - no more than 0.3%
• arsenic - not higher than 0.08%;
• manganese – 0.35% – 0.65%;
• chromium – not higher than 0.25%;
• silicon – 0.17% – 0.37%;
• sulfur and phosphorus - respectively, no more than 0.040% and 0.035%.

Characteristics of material 20L

Brand: 20L Substitute: 25L, 30L

Classification: Casting steel, unalloyed

Application: chabots, fittings, shaped castings of general mechanical engineering parts produced by the lost wax method, parts of welded cast structures and other parts operating at temperatures from -40 to 450 °C.

Types of supply of material 20L

Chemical composition in % of material 20L GOST 977 - 88

C Si Mn S P0.17 — 0.250.2 — 0.520.45 — 0.9 to 0.06 to 0.06

The temperature of the critical points of the material is 20L.

Ac1 = 735, Ac3(Acm) = 854, Ar3(Arcm) = 835, Ar1 = 680 Technological properties of material 20L.

Foundry and technological properties of material 20L.

Heat treatment modes for 20L material

Mechanical properties at T=20oC of material 20L.

Physical properties of material 20L.

Foreign analogues of material 20L

Attention! Both exact and closest analogues are indicated.
1.0443

Designations:

Technological properties

Steel 20 is a high-tech alloy classified as cemented. The cementation process is the saturation of the surface of a product with carbon by heating in a special environment. As a result of this treatment, the top layer of the product acquires a hardness value of up to 62 HRC, which is three times higher than that of the core. The metal lends itself well to forging, cutting and soldering, is not prone to cracking, and retains high density. All popular methods are applicable for welding - ADS, KTS, RDS, submerged arc welding, etc. The type of equipment depends on the selected welding technology.

Impact strength of steel 20 KCU (J/cm3) at low temperatures °C

Steel yield strength 20

Hardness

Application of steel 20

Steel 20 is used for the manufacture of:

• pipes and pipe fittings, hooks and other parts operated under conditions of high pressure and temperatures from -40°C to 450°C;
• thin spare parts used in conditions of increased abrasion;
• stops, gears, fingers and other parts that are used under low load;
• welded profiles;
• (after chemical-thermal treatment) parts that require enhanced surface strength, but not the core (gears, worms, etc.).

Physical properties

The melting point of steel 20 is 1500C, steel becomes liquid at 1600C. Steel 20 has good thermal conductivity and heat capacity. The modulus of elasticity, coefficient of thermal expansion, thermal conductivity, density, specific heat capacity and electrical resistivity for various temperatures are shown in the table below.

Physical properties of the material 20 .

physical characteristics